fa گروه سرامیک Ceramic Materials and Engineering Research Paper Research Paper An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (&#963-&#949) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction.It was shown that, both the magnitude of plastic strains and the depth of plastic deformed zones increased with the applied load. The material exhibited considerable work softening in addition to work hardening at the highest applied load. The softened layer placed just beneath the mechanical mixed layer (MML), was mostly covered with the fine fractured eutectic Si and TiC fragments most of which were associated with microcracks at Al/Si and Al/TiC interfaces. The results were discussed in terms of some of the current work hardening models. Plastic deformation, Worn surface, Composite, AI,TiCp composite 9 15 http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1-15&slc_lang=fa&sid=1 SAGHAFIAN LARIJANI H. 1800319475328460039 1800319475328460039 Yes RAINFORTH W. M. 1800319475328460040 1800319475328460040 No