Iranian Journal of Materials Science and Engineering

Abstract:

composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at

800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nano

powder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-

Teller (BET) techniques. It was demonstrated that the formation temperature decreased to 850

particles revealed an average size of 30 nm with a narrow size distribution. The mechanism of MgAl

was found to be a template type where the morphology and size of product were similar to those of alumina formed

from boehmite decomposition. Prolonging the reaction time from 0.5 to 3 h, the reaction was further completed and

crystallinity was improved. However, the increase of temperature was more effective in this regard.