A. Khavasfar1,, M. H. Moayed2, M. M. Attar3,
Volume 4, Issue 3 (12-2007)
Abstract
Abstract: The performance of an Imidazoline based commercial corrosion inhibitor in CO2
corrosion of a gas-well tubing steel was studied by employing Electrochemical Impedance
Spectroscopy (EIS) technique. Inhibitor performance was investigated by means of its efficiency at
various concentration and also its behavior at various exposure time. EIS results showed that
inhibitor interaction to the electrode surface obeys Lungmuir adsorption isotherm. Interpretation
of some parameters such as Rct, Rpf, Cdl, and Cpf associated to the equivalent circuit fitted to the
experimental rsults showed that not only inhibitor efficiency and surface coverage improve by
increasing in inhibitor concentration in the solution but also at constant inhibitor concentration
both surface coverage and efficiency improve with exposure time and reach to their highest value
after 4 hours.
Z. Ghaferi, K. Raeissi, M. A. Golozar,, A. Saatchi, S. Kabi,
Volume 7, Issue 4 (10-2010)
Abstract
Abstract:
current densities. Electrochemical impedance spectroscopy (EIS) results showed that the codeposition mechanism of
tungsten in Ni-W deposition is the reduction of tungsten oxide which changed to the reduction of tungsten-containing
ion complexes at higher current densities. In Co-W electrodeposition, the tungsten codeposition takes place via
reduction of tungsten oxide, although, the role of tungsten-containing complexes at higher current densities cannot be
ruled out. The surface morphology of Ni-W coatings was crack-free and was strongly dependent on deposition current
density. In addition, higher grain size and lower tungsten content were obtained by increasing the current density. In
Co-W coatings, no obvious variation in surface morphology was observed except for the fine cracks appeared at
higher current densities. In this system the grain size remained almost constant with increasing current density. The
microhardness values of Ni-W and Co-W coatings decreased due to the increase in the grain size and/or decrease in
tungsten content.
Ni-W and Co-W alloy nanocrystalline coatings were electrodeposited on copper substrate at different
Sh. Shahriari, M. Ehteshamzadeh,
Volume 10, Issue 1 (3-2013)
Abstract
Abstract: Plasma electrolytic oxidation (PEO) technique was used to prepare ceramic coatings on the casted aluminum alloys containing ~5 and ~9.5 wt.% Mg. The applied voltage was controlled at 450V and 550V for evaluating the effect of this main parameter, as well as, magnesium content of the substrate on the microstructure and electrochemical corrosion behavior after PEO treating. The results of X-ray diffraction confirmed formation of galumina and MgSiO3. It was found that higher applied voltage caused fewer and minor discharge channels which led to higher corrosion resistance. Also, increasing of magnesium content of the substrate caused decreasing of polarization resistance, which could be associated to the formation of MgSiO3.
Yemurai Vengesa, Arash Fattah-Alhosseini, Hassan Elmkhah, Omid Imantalab,
Volume 18, Issue 4 (12-2021)
Abstract
The main purpose of this investigation is to assess the effect of post-deposition annealing treatment on the electrochemical behavior of TiN coating developed on AISI 304 stainless steel substrate using cathodic arc evaporation physical vapor deposition (CAE-PVD). Post-annealing treatment at 400 ºC was performed on the coated substrate for 1 h. The studied samples were characterized using X-ray diffraction (XRD), scanning electron microscope (SEM), potentiodynamic polarization (PDP), and electrochemical impedance spectroscopy (EIS) tests. The preferred orientation of TiN (111) was identified by XRD patterns and the crystallinity of the coating increased after annealing treatment. SEM observations indicated that TiN coatings free of cracks were successfully developed on the substrate. The electrochemical measurements elucidated that the annealed coating had better corrosion resistance compared to that of the as-deposited coating with a lower current corrosion density. This investigation implied that improved corrosion performance of the TiN coating can achieved by performing post-deposition annealing treatment.
Mozhgan Hirbodjavan, Arash Fattah-Alhosseini, Hassan Elmkhah, Omid Imantalab,
Volume 19, Issue 4 (12-2022)
Abstract
The principal goal of this research is to produce a CrN/Cu multilayer coating and a CrN single-layer
coating and also compare their electrochemical and antibacterial behavior. In this investigation, the coatings were
applied to the stainless steel substrate by cathodic arc evaporation a sub-division of physical vapor deposition
(CAE-PVD). The present phases were characterized and the thickness of the coatings was measured using X-ray
diffraction (XRD) and field emission scanning electron microscopy (FE-SEM), respectively. Rockwell-C tester was
used to evaluate the adhesion quality. Also, to evaluate the mechanical properties of the coatings such as modulus
of elasticity and hardness, a nanoindentation test was used and the indentation effect and coating topography were
evaluated using atomic force microscopy (AFM). Studying the electrochemical behavior of the coatings was done
using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP) tests in Ringer's
solution. The results of EIS tests showed that the CrN coating had higher polarization resistance in comparison to
the CrN/Cu coating and an increasing trend of polarization resistance related to both coatings was identified by
rising the time of immersion. Also, using the PDP curves, the CrN and CrN/Cu coating current densities were
estimated at 1.835×10-8 and 2.088×10-8, respectively. The antibacterial activity of CrN and CrN/Cu coatings was
evaluated by the spot-inoculation method. The results of the antibacterial test indicated that compared to CrN
coating, CrN/Cu coating had a better impact on the control of the bacteria growth.