. S. Khani, . M. T. Salehi, . H. R. Samim, Prof. M. R. Aboutalebi, . H. Palkowski,
Volume 13, Issue 3 (September 2016)
Abstract
The evolution of microstructure and mechanical properties of a magnesium cast alloy (AZ31) processed by equal channel angular pressing (ECAP) at two different temperatures were investigated. The as-cast alloy with an average grain size of 360 was significantly refined to about 5 after four ECAP passes at 543 K. Grain refinement was achieved through dynamic recrystallization (DRX) during the ECAP process in which the formation of necklace-type structure and bulging of original grain boundaries would be the main mechanisms. ECAP processing at lower temperature resulted in finer recrystallized grains and also a more homogenous microstructure. The mechanical behavior was investigated at room temperature by tensile tests. The obtained results showed that the ECAP processing can basically improve both strength and ductility of the cast alloy. However, the lower working temperature led to higher yield and ultimate strength of the alloy.
Parviz Parviz Mohamadian Samim, Arash Fattah-Alhosseini, Hassan Elmkhah, Omid Imantalab,
Volume 19, Issue 1 (March 2022)
Abstract
In this study, CrN/ZrN multilayer nanostructured coatings with different bilayers (10, 20, and 30) were created by the cathodic arc evaporation. The electrochemical behavior of samples was evaluated by polarization and impedance spectroscopy tests in the Ringer medium and the pin on disk test was used to investigate the tribological behavior of the samples. The results of measurements showed that the electrochemical and tribological behavior of the coatings depends on the number of bilayers and by rising the number of bilayers, the coating shows higher corrosion resistance and better tribological performance. Field emission scanning electron microscopy (FE-SEM) images of the specimens after exposure to the corrosion medium showed that the number of surface cavities were formed by the coating that had the highest number of bilayers comparing with other coatings were quite fewer in number and smaller in diameter. The results of the pin on disk test showed that by increasing the number of bilayers from 10 to 30, the coefficient of friction and wear rate decreased and the 30L coating showed better wear resistance.