Showing 3 results for SAREMI M.
Dehghanian C., Saremi M., Mohammadi Sabet M.,
Volume 2, Issue 1 (Oct 2005)
Abstract
The synergistic behavior of molybdate and phosphate ions in mitigating the corrosion of mild steel in simulated cooling water was evaluated performing potentiodynamic polarization and impedance spectroscopy tests. Phosphate and molybdate showed a synergistic effect on corrosion inhibition of steel in simulated cooling water. The observed reduction in anodic and cathodic current densities could be the consequence of incorporation of both phosphate and molybdate ions in forming a protective layer on the surface. The charge transfer resistance of the protective layer formed on steel surface was much greater in presence of both ions in solution than that when each inhibitor used alone.
Saremi M., Nouri Delavar A., Kazemi M.,
Volume 2, Issue 4 (Jul 2005)
Abstract
An investigation of the electrochemical noise generation during Stress Corrosion Cracking (SCC) of 70-30 Brass in Mattson's solution was conducted. The fluctuations of potential and current were monitored. The relationship between potential and current fluctuations has been evaluated in time domain and the obtained data has been analyzed in the frequency domain using Power Spectral Density (PSD). It is shown that 70-30 Brass has characteristic noise behavior during SCC that is step-by-step change in current and potential up to the final stage of fracture, and this may be used for SCC monitoring.
Saremi M., Motaghi Golshan B.,
Volume 3, Issue 3 (Jul 2006)
Abstract
A film of osteoconductive and biocompatible material on biomedical metallic implants can create bioactivity of the implant and shorten healing time. Hydroxyapatite, that is the most important mineral part of human bone, was coated on Ti6Al4V using cathodic electrode position process. Pulse electrode position technique was used and the effects of different parameters such as potential, duty cycle (on time/ (on time+ off time)), temperature and current density on the morphology of the deposits were examined. Nano size deposits were formed under controlled temperature and optimization of voltage and current density.