Hannaneh Ghadirian, Hamid Golshahi, Sara Bahrami, Farhood Najafi, Allahyar Geramy, Soolmaz Heidari,
Volume 19, Issue 2 (June-Biomaterials Special Issue- 2022)
Abstract
Quaternary ammonium compounds (QACs) are among the most commonly used antibacterial agents. The aim of this study was to synthesize a dimethacrylate monomer functionalized with a QAC and to study its effect on the properties of an orthodontic adhesive primer. Urethane dimethacrylate monomer functionalized with a QAC (UDMAQAC) was synthesized and then characterized by nuclear magnetic resonance spectroscopy (NMR) and Fourier transform infrared spectroscopy (FTIR). 5, 10, 15 and 20 wt% of UDMAQAC was added to an orthodontic adhesive primer (control group). FTIR analysis was used to measure the degree of conversion (DC). The bond strength of dental brackets was measured by shear bond strength (SBS) test and adhesive remaining index (ARI) was evaluated by stereomicroscope. Agar diffusion test and MTT assay were used to evaluate the antibacterial property and cell viability, respectively. Statistical analysis included one-way ANOVA with Tukey’s post hoc test and Kruskal-Wallis nonparametric test (P˂0.05). Although the obtained data did not show significant differences between the SBS and DC of different groups, but the highest values were obtained by adding 10 wt% monomer. Adding more than 10 wt% UDMAQAC resulted in significant increase in antibacterial property. The 15 and 20 wt% groups showed significantly lower cell viability
Ali Hasanzade Salmasi, Mahban Zarei, Shadab Safarzadeh Khosroshahi, Soolmaz Heidari, Farhood Najafi, Mojtaba Ghomayshi, Katayoun Lesani,
Volume 20, Issue 3 (September 2023)
Abstract
Amorphous calcium phosphate (ACP) which is a transient phase in natural bio-mineralization process has recently gained the spotlight. This study aimed to assess the effect of incorporation of nano-ACP (NACP) in a dental adhesive with/without surface treatment with silane coupling agent on bond strength. NACP was synthesized by the wet chemical precipitation technique. To characterize the structure of NACP, X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy were used. Forty molars were randomized into 4 groups of 10. The teeth were restored with composite resin and the bonding agent (one of the four groups). Adper Single Bond 2 was used as the control group. In 4wt% NACP group, NACP fillers were added to the bonding agent. In 0.4wt% and 4wt% SNACP groups, silanized NACP fillers were added to the bonding agent. Finally, the mode of failure of specimens was determined. Data were analyzed by one-way ANOVA and Tukey's post-hoc tests. P<0.05 was considered statistically significant. Addition of 4wt% non-silanized NACP decreased the bond strength compared with the control group (P<0.05). The bond strength of the groups with silanized fillers was not significantly different from that of the control group. Addition of silanized NACP to dental adhesive had no significant adverse effect on bond strength, which is a promising finding to pave the way for the synthesis of bonding agents containing bioactive fillers.