Salma Bessalah, Jebahi Samira, Amel Raoufi, Asim Faraz, Mouldi Zagrouba, Mohamed Hammadi,
Volume 19, Issue 2 (June-Biomaterials Special Issue- 2022)
Abstract
Abstract
Gelatin (GEL) is most extensively used in various fields, particularly in therapeutics and pharmaceuticals. GEL was extracted from goat skin using hot temperature extraction process and compared with that of commercial GEL. The physico-chemical characterization and functional properties were investigated by using temperature denaturation (Td), water-holding and fat-binding capacities (WHC and FBC), colour measurement and UV-light spectrum. In vitro biocompatibility was studied for the first time and was evaluated by blood coagulation index (BCI) and haemolytic tests for using as wounds dressing. The results revealed thermal stability of goat GEL at Td 37°C. WHC and FBC capacities represented 2.5 and 1.2 g/ml, respectively. The hunter colour spaces a*, b* and L* showed a -0.27, -1.97 and 25.23 values, respectively. UV-Vis absorption spectrum of the goat GEL showed a maximum absorption peak at 280 nm. The in vitro anticoagulant activities of extracting GEL were higher than 70% after incubation for one hour. After being in contact with red blood cells for 1 h, the haemolysis ratio increased from to 0.46 to 1.4 when the concentration of goat GEL increased from 1 to 50 mg/ml suggesting the safety of the tested samples. These results suggest that thromboresistivity and hemocompatibility of this biopolymer retained the biological activity of our samples for biomaterial applications. According to this, goat GEL successfully competes with, and significantly could be useful for substitution of bovine in wound healing.
Faraz Hussain, Muhammad Umar Manzoor, Muhammad Kamran, Tahir Ahmad, Fahad Riaz, Sehrish Mukhtar, Hafiz Muhammad Rehan Tariq, Muhammad Ishtiaq,
Volume 21, Issue 0 (IN PRESS 2024)
Abstract
Magnesium alloys are increasingly valued for biomedical applications due to their biocompatibility. This study investigates Mg-AZ31B alloy samples treated with quartz and alumina grits (<200 μm) at varied pressures, followed by anodization in an eco-friendly alkaline electrolyte. The results show that increased blasting pressure produces a rougher surface. Anodization time significantly affects the thickness of the anodic film, leading to a transition in surface morphology from fine to coarse structures with complete film coverage. Characterization by XRD reveals that the anodic film mainly comprises magnesium oxide and hydroxide phases. Open Circuit Potential (OCP) measurements demonstrate enhanced corrosion resistance post-anodization, particularly notable at 40 minutes on alumina-blasted samples. ANOVA confirms that both blasting pressure and anodization time significantly influence coating thickness and OCP, indicating the formation of a dense anodized layer.