Foadian F, Soltanieh M, Adeli M, Etminanbakhsh M. THE FORMATION OF TiAl3 DURING HEAT TREATMENT IN EXPLOSIVELY WELDED Ti-Al MULTILAYERS. IJMSE 2014; 11 (4) :12-19
URL: http://ijmse.iust.ac.ir/article-1-716-en.html
URL: http://ijmse.iust.ac.ir/article-1-716-en.html
Abstract: (17740 Views)
Metallic-intermetallic laminate (MIL) composites are promising materials for structural applications especially in the aerospace industry. One of the interesting laminate composites is the Ti-TiAl 3 multilayer. In this work, commercially pure sheets of aluminum and titanium with almost equal thickness of around 0.5 mm were explosively joined. The achieved multilayers were annealed at 630 ℃in different times so that an intermetallic layer was formed at the Ti/Al interface. The resulting microstructure was studied by optical and scanning electron microscopy and Energy Dispersive Spectroscopy (EDS). TiAl3 was the only intermetallic phase that was observed in all annealing times. The kinetics of the formation of TiAl 3 was investigated and compared to previous research studies performed on Ti-Al multilayers which were fabricated using methods other than explosive welding.
Type of Study: Research Paper |
Subject:
materials engineeing and special subjects
Send email to the article author
| Rights and permissions | |
 |
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License. |